名称:SIS1105 巴陵石化热塑性橡胶
编号:Pro2018327173523
型号:SIS1105
价格:14000
厂商:巴陵石化(岳阳石化)
时间:2018/3/27 17:38:09
购买:
SIS1105岳阳巴陵石化热塑性弹性体(苯乙烯-异戊二烯嵌段共聚物)
牌号:SIS1105             
产品性能
外观:白色或浅色,不含机械杂质及油污
结构:线型
密度:880~930kg/m3(20℃)
SI含量(%):0
嵌段比SI:15/85
挥发份(质量分数) %:≤0.70
25度、25%甲苯溶液粘度(mPa.s):1100-1600
拉伸强度(≥MPa):12
扯断伸长率(≥%):1050
熔体质量流动速率(g/10min):8.0~12
邵氏硬度(A):35~50
主要应用领域:胶带、标签、塑料改性等。制备通用压敏胶带,初粘性好、持粘时间长。
岳阳市巴陵佳云石化有限公司长期备有现货。
包装:20 公斤纸塑包装袋或520 公斤聚丙烯集装袋
运输:在运输过程中,应采取措施防止日光直接照射和雨水浸泡,运输车辆应整洁、避免包装破损和杂物混入,不属于危险品。
贮存:苯乙烯-异戊二烯嵌段共聚物(SIS)产品应贮存在通风、干燥、清洁并保持有良好消防设施的仓库内。贮存时,应成行成垛整齐堆放,并保持一定行距,远离热源,并防止阳光直接照射,严禁在露天堆放。贮存期从生产之日起,一般不超过24个月。
 
 
Yueyang Baling Petrochemical thermoplastic elastomer (styrene isoprene block copolymer) sis1105
Brand: sis1105
Product performance
Appearance: white or light color, without mechanical impurities and oil stains
Structure: linetypes
Density: 880 ~ 930kg / m3 (20 ℃)
Si content (%): 0
Block ratio Si: 15 / 85
Volatile matter (mass fraction)%: ≤ 0.70
25 ℃, 25% toluene solution viscosity (MPa. S): 1100-1600
Tensile strength (≥ MPa): 12
Elongation at break (≥%): 1050
Melt mass flow rate (g / 10min): 8.0 ~ 12
Shore hardness (a): 35 ~ 50
Main application fields: tape, label, plastic modification, etc. The preparation of general pressure-sensitive adhesive tape has good initial adhesion and long holding time.
Yueyang Baling Jiayun Petrochemical Co., Ltd. has long-term stock.
Packing: 20kg paper plastic bag or 520kg polypropylene container bag
Transportation: in the process of transportation, measures should be taken to prevent direct sunlight and rain water immersion. Transport vehicles should be clean and tidy, and avoid package damage and sundries mixed in. They are not dangerous goods.
Storage: styrene isoprene block copolymer (SIS) products should be stored in a ventilated, dry, clean warehouse with good fire protection facilities. During storage, they should be stacked in rows and stacks in order, with a certain distance between lines, away from heat sources, and direct sunlight should be prevented. It is strictly forbidden to stack them in the open air. The storage period shall not exceed 24 months from the date of production.